牌号
项目（名称） |
|
刚玉质GPA-90 |
特级高铝质TA-85 |
一等高铝A-75 |
二三等高铝LQ-55
LQ-53 |
粘土质NQ-42 |
铝镁火泥AM-70 |
镁铝火泥
M-ML43 |
尖晶石火泥MA-70 |
铝碳火泥
AC-60 |
锆质火泥GZ-50 |
奠来石硅线石火泥GS |
粘土轻质火泥 |
|
Al2O3，% |
≥ |
90 |
85 |
75 |
55 53 |
42 |
50 |
42 |
70 |
50 |
ZRO250 |
56 |
40 |
|
Mgo，% |
≥ |
|
|
|
|
|
30 |
43 |
8 |
C：6 |
|
|
|
|
耐火度，℃ |
≥ |
1790 |
1790 |
1790 |
1770 |
1710 |
1790 |
1790 |
1790 |
1790 |
1790 |
1790 |
1650 |
|
粘结时间，min |
|
1～3 |
1～3 |
1～3 |
1～3 |
1～3 |
1～3 |
1～3 |
1～3 |
2～5 |
1～3 |
1～3 |
1～3 |
粘
结
强
度
Mpa |
110℃×24h |
≥ |
2 |
2 |
1.0 |
1.0 |
1.0 |
1.0 |
1.5 |
1.0 |
0.7 |
1.0 |
1.0 |
0.8 |
|
1500℃×24h |
≥ |
5 |
6 |
6 |
|
|
|
|
|
|
|
|
|
|
1400℃×24h |
≥ |
|
|
|
4 |
|
5 |
|
|
|
|
|
|
|
1400℃×24h |
≥ |
|
|
|
|
|
|
|
6 |
|
3.0 |
3.0 |
|
|
1200℃×24h |
≥ |
|
|
|
|
|
|
|
|
|
|
|
1.0 |
|
1200℃×24h |
≥ |
|
|
|
|
3.0 |
|
|
|
|
|
|
|
粒
度 |
≤0.5mm |
≥ |
97 |
97 |
97 |
97 |
97 |
|
|
|
|
|
|
|
|
≤0.074mm |
≥ |
50 |
50 |
50 |
50 |
50 |
|
|
|
60 |
50 |
60 |
50 |
|
0.5～1mm |
≤ |
|
|
|
|
|
|
|
|
12 |
|
|
|
|
＞1mm |
不准有 |
|
应用范围 |
配用相应材质的定型产品 |
|
|
| |
|
粘土结合浇注料理化指标 |
名称
项目 |
|
粘土结合浇注料理化指标 |
牌号
|
|
NL2 |
NL1 |
NN |
Al2O3，%
|
≥ |
65 |
60 |
55 |
|
Mgo，% |
≥ |
|
|
|
|
SiO2，% |
≤ |
|
|
|
|
耐火度，℃ |
|
1730 |
1730 |
1710 |
|
体积密度，g/cm3 |
≥ |
2.3 |
2.25 |
2.25 |
|
烧后线变化率 |
1450℃×3h |
|
±0.5 |
|
|
|
1400℃×3h |
|
|
|
|
|
1350℃×3h |
|
|
±0.5 |
|
|
1300℃×3h |
|
|
|
±0.5 |
|
耐压强度Mpa |
110℃×24h |
≥ |
10 |
3 |
2 |
|
1000℃×3h |
≥ |
|
|
|
|
1400℃×3h |
≥ |
|
|
|
抗折
强度
Mpa |
110℃×24h |
≥ |
2.0 |
0.5 |
0.4 |
|
1000℃×3h |
≥ |
|
|
|
|
1400℃×3h |
≥ |
|
|
|
|
最高使用温度,℃ |
|
1450 |
1450 |
1350 |
|
应用范围 |
加热炉和均热炉等 |
|
|
钢包和钢纤维浇注料理化指标 |
名称
项目 |
|
大钢包浇注料理化指标 |
中小钢包浇注料理化指标 |
钢纤维增强浇注理化指标 |
|
牌号 |
|
|
|
刚玉质KIP |
高铝质A-85 |
高铝质
A-70 |
|
Al2O3，% |
≥ |
90 |
75 |
90 |
80 |
70 |
|
Mgo，% |
≥ |
4～10 |
10 |
|
|
|
|
耐火度，℃ |
|
|
|
1790 |
1790 |
1790 |
|
体积密度，g/cm3 |
≥ |
3.0 |
2.8 |
3.0 |
2.8 |
2.6 |
|
耐压强度Mpa |
110℃×24h |
≥ |
35 |
25 |
80 |
80 |
70 |
|
1100℃×3h |
≥ |
25 |
20 |
90 |
80 |
70 |
|
1300℃×3h |
≥ |
40 |
40 |
|
|
|
|
1500℃×3h |
≥ |
50 |
50 |
100 |
60 |
60 |
|
1650℃×3h |
≥ |
60 |
|
|
|
|
|
烧后线变化率 |
110℃×24h |
± |
|
|
0.1 |
0.1 |
0.1 |
|
1500℃×3h |
|
|
±0.8 |
0～±2 |
±1.0 |
±1.0 |
|
1650℃×3h |
|
0.2～0.4 |
|
|
|
|
抗折
强度
Mp |
110℃×24h |
≥ |
4 |
4.0 |
4.0 |
5.0 |
5.0 |
|
1400℃×.5h |
≥ |
7 |
|
|
5.0 |
5.0 |
|
最高使用温度,℃ |
|
|
|
1700 |
1650 |
1600 |
|
使用范围 |
|
钢包中间包 |
喷枪,钢包底,回转窗,冲击板,档渣堰,电炉顶三角区,出铁沟,均热炉,沟盖等 |
|
| |
|
低水泥浇注料理化指标 |
|
项目 牌号 |
|
JA-90 |
JA-80 |
JA-70 |
JA-65 |
JA-55 |
|
Al2O3，% |
≥ |
90 |
80 |
70 |
65 |
55 |
|
耐火度，℃ |
≥ |
1790 |
1790 |
1730 |
1710 |
1710 |
|
体积密度，g/cm3 |
≥ |
2.85 |
2.75 |
2.65 |
2.35 |
2.2 |
|
烧后线变化率 |
1500℃×3h |
≥ |
±0.5 |
±0.5 |
±1.0 |
|
|
|
1450℃×3h |
≥ |
|
|
|
±1.0 |
|
|
1400℃×3h |
≥ |
|
|
|
|
±1.0 |
|
耐压强度Mpa |
110℃×24h |
≥ |
80 |
50 |
40 |
30 |
25 |
|
1100℃×3h |
≥ |
90 |
60 |
45 |
35 |
40 |
|
1450℃×3h |
≥ |
|
|
50 |
45 |
|
|
1500℃×3h |
≥ |
100 |
80 |
|
|
40 |
抗折
强度
Mpa |
110℃×24h |
≥ |
5.0 |
4.0 |
4.0 |
4.0 |
3.0 |
|
1500℃×3h |
≥ |
8.0 |
4.0 |
5.0 |
|
|
|
1450℃×3h |
≥ |
|
|
|
4.0 |
|
|
1400℃×3h |
≥ |
|
|
|
|
3.5 |
|
最高使用温度,℃ |
|
1600 |
1600 |
1500 |
1500 |
1400 |
|
应用范围 |
|
相对高温度的钢包包底PH浸渍管,加热炉烧嘴,回转炉,中间包等各种窑炉 |
|
|
轻质耐火浇注料理化指标 |
|
项目 牌号 |
|
PM-0.5 |
PM-0.8 |
PM-1.0 |
PM-1.5 |
|
Al2O3，% |
≥ |
23 |
33 |
27 |
55 |
|
SiO2，% |
≤ |
45 |
23 |
54 |
|
|
体积密度，g/cm3 |
|
0.5±0.05 |
0.8±0.05 |
1.0±0.05 |
1.5±0.05 |
|
烧后线变化率 |
1000℃×3h |
|
±0.6 |
±O.8 |
|
|
|
1250℃×3h |
|
|
|
±1.0 |
±1.0 |
|
耐压强度Mpa |
常温 |
|
1.0 |
3.0 |
4.0 |
10 |
|
1100℃×3h |
|
0.8 |
2.5 |
5 |
15 |
|
1250℃×3h |
|
|
|
|
8.0 |
抗折
强度
Mpa
|
常温 |
|
0.3 |
1.0 |
1.2 |
3.0 |
|
1000℃×3h |
|
0.2 |
0.8 |
1.0 |
|
|
1250℃×3h |
|
|
|
|
2.0 |
|
导热系数W/m,K |
250℃ |
0.17 |
0.2 |
0.26 |
0.34 |
|
500℃ |
0.20 |
0.23 |
0.3 |
0.38 |
|
应用范围 |
各种窑炉工作层或隔垫层，其使用温度参照烧后线变化的温度 |
|
|
|
| |
|
高炉出铁沟用浇注料、捣打料理化指标
|
牌号
项目 |
|
JL-1 |
JL-2 |
DL-1 |
DL-2 |
|
材质 |
|
浇注料 |
捣打料 |
Al2O3，%
|
≥ |
65 |
50 |
45 |
45 |
Sic，%
|
≥ |
8 |
30 |
10 |
20 |
F.C，%
|
≥ |
3 |
4 |
|
|
体积密
度，g/cm3 |
110℃×2h |
≥ |
2.70 |
2.55 |
|
|
|
1450℃×2h |
≥ |
2.60 |
2.50 |
2.0 |
2.35 |
|
耐压强度Mpa |
110℃×2h |
≥ |
5.0 |
6.0 |
|
|
|
1450℃×2h |
≥ |
15.0 |
10.0 |
|
|
冷态
抗折
Mpa
|
110℃×2h |
≥ |
2.5 |
2.0 |
2.0 |
2.0 |
|
1450℃×2h |
≥ |
4.5 |
4.0 |
|
|
|
烧后线变化率% |
|
(1450℃×2h)±0.5 |
(1450℃×2h)±0.5 |
(1450℃×2h)±0.5 |
(1450℃×2h)±0.5 |
应用范围(中型高炉)
|
|
出铁沟铁水线 |
出渣沟渣线 |
出铁沟铁水线 |
出渣沟 |
|
|
喷补料、中间包涂料理化指标 |
名称
项目 |
中间包涂料 |
喷补料 |
|
材质 |
镁钙质 |
高铝质 |
粘土质 |
镁质 |
铝碳化硅质 |
|
Al2O3，% |
|
≥55 |
≥40 |
|
≥370 |
|
MgO2，% |
≥65 |
|
|
≥78 |
|
|
CAO，% |
≥15.0 |
|
|
|
SIC≥8 |
|
体积密度，g/cm3 |
≥2.2 |
≥2.2 |
≥2.0 |
≥2.4 |
≥2.3 |
|
耐压强度Mpa |
110℃×24h |
≥10 |
|
(1370℃,
10h)≥20
|
|
|
|
1000℃×3h |
1370℃,
10h |
(800℃,
10h)≥20 |
|
|
|
|
1400℃×3h |
≥8.0 |
1370℃,10h
≥20 |
|
1370℃,10h
≥20 |
1370℃,10h
≥20 |
抗折
强度
Mpa
|
110℃×24h |
|
|
|
|
|
|
1000℃×3h |
|
|
|
|
|
|
1400℃×3h |
|
|
|
|
|
|
烧后线变化率% |
1500℃,
10h)
＜-2.5 |
|
|
|
|
|
应用范围 |
中间包 |
高炉加热炉石灰窑等 |
高炉加热炉石灰窑等 |
电炉转炉等 |
鱼雷罐 |
|
| |
| |